海上油田剖面调整用分散共聚物颗粒体系的研制

Development of Dispersed Copolymer Particle System for Profile Control in Offshore Oilfield

于萌 铁磊磊 李翔 刘文辉

YU Meng TIE Leilei LI Xiang LIU Wenhui

中海油田服务股份有限公司油田生产事业部，天津 300450

Oilfield Production Division, China Oilfield Services Limited, Tianjin, 300450, China

为了对海上油田中高含水期非均质油层进行剖面调整，以丙烯酰胺（AM）为主剂，N, N亚甲基双丙烯酰胺（MBA）为交联剂，合成了网状结构的高黏聚合物，经研磨控制技术处理后，制得分散共聚物颗粒体系。试验结果表明，在AM质量分数（5%）和AM/MBA质量比（250∶1）一定的条件下，研磨速率和研磨时间对粒径分布影响较大。封堵运移性能评价试验结果表明，分散共聚物颗粒体系具有良好注入性、深部运移能力及封堵性能，在等用量条件下，分散共聚物颗粒的封堵能力显著优于聚合物凝胶。研究表明，研制的分散共聚物颗粒粒径分布宽，纳米至微米级别可控，且可实现在线注入，具有制备工艺简单、成本低、抗高温和环保等特点，对海上中高含水期油田剖面调整具有较好的适用性，可在现场推广应用。

A high-viscosity polymer was developed in order to adjust the profile of heterogeneous offshore oilfields in the middle-high water cut period. Performance advantages were achieved by taking acrylamide (AM) as the main agent and N, N methylenebisacrylamide (MBA) as the crosslinker. This polymer can be processed by the grinding control technology to obtain a dispersed copolymer particle system. The experimental results showed that the grinding rate and grinding time had a large impact on the particle size distribution for the given monomer mass fraction (5%) and the AM/MBA mass ratio of 250 to 1. The results of plugging and migration experiment under simulated formation conditions indicated that the dispersed copolymer particle system had good injectability, deep migration ability and plugging performance. For the given dosage, the plugging ability of dispersed copolymer particles was significantly better than that of the polymer gel. The research suggested that the particle size distribution of this system was wide and controllable in the nanometer to micrometer level, making online injection possible. The system has the advantages of simple formulating process, low cost, temperature resistance and environmental protection, etc. It possesses good applicability in offshore oilfields for the profile control in the middle-high water cut period, and can be promoted and applied in oilfields.

中国海油支持项目“智能控释型调–堵–驱复合EOR体系研发”（编号：E-23197022）部分研究内容，2017年天津市留学回国人员择优资助项目

https://doi.org/10.11911/syztjs.2020019